Nanosized structural transformation and nonlinear optical properties of lithium niobium germanate glassesстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Glass formation in Li2O-Nb2O5-GeO2 (LNG) system, the structure and crystallization behavior of glasses that have compositions near the ratio Li2O/Nb2O5 similar to 1 corresponding to stoichiometry of ferroelectric phase LiNbO3 were examined by differential thermal analysis, X-ray diffraction, small-angle neutron scattering and second harmonic generation (SHG). LNG glasses were subjected to heat treatments at temperatures in the range between T-g and temperature of the first exothermic peak in order to initiate nonlinear optical activity by nanoheterogeneity formation. Transparent nanostructured glasses with second-order optical nonlinearity were obtained for compositions characterized by the Li2O/Nb2O5 molar ratio ranging from 0.83 to 1.2 and GeO2 40-45 mol%. As prolonged heat treatments of nanostructured glasses result in crystallization of ferroelectric LiNbO3 the origin of SHG in transparent LNG glasses is supposed to be connected predominantly with polarity of nanoheterogeneities formed at the initial stage of phase separation. (C) 2007 Elsevier B.V. All rights reserved.