Effect of Adding Porcelain on Properties of Porous Ceramic Based on Electromelted Corundumстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 19 февраля 2018 г.
Аннотация:Porous permeable ceramic is prepared from electromelted corundum (EMC) with fineness of about 0.5 mm with added porcelain. Compositions are prepared with different ratios of EMC/porcelain: 99/1, 97/3, 95/5, 93/7, and 90/10. Specimens in the form of bars with a size of 40 _ 7 _ 6.5 mm are prepared by uniaxial semidry compaction under a pressure of 25 and 50 MPa and fired at 1350 and 1450°C. Specimen open porosity varies from 22 to 30%, and ultimate strength in bending from 1.1 to 9.3 MPa. Porous ceramic is promising for filters and ceramic membrane substrates.