Synthesis and properties of calcium hydroxyapatite/carbon fiber compositesстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 2 февраля 2018 г.
Аннотация:10.1134/S0036023617090200
Аннотация
Composites comprising micrometer-sized carbon fibers (CFs) and biocompatible nanocrystalline calcium hydroxyapatite Ca-10(PO4)(6)(OH)(2) (HA, NCHA), containing 1.0, 2.0, and 5.0 wt % CFs, have been synthesized in the course of precipitation from aqueous solutions in the Ca(OH)(2)-H3PO4-CF-H2O system. Some physicochemical characteristics of the precursor CFs and synthesis products have been determined using chemical, X-ray diffraction, and thermal analyses, IR spectroscopy, and scanning and transmission electron microscopy. An analysis of composition-synthesis conditions-structure-particle size-property correlations indicates that the presence of CFs in HA/CF composites strongly decreases the sizes and modifies the habit of NCHA. A rise of CF content in the HA/CF composite is accompanied by a decrease in particle size and a rise in solubility of NCHA.