The pulse laser processing of metal thin films on glass substrates

Mikheev, G.M.; Zonov, R.G.; Kaluzhny, D.G.

Авторы: Mikheev G.M., Zonov R.G., Kaluzhny D.G.
Сборник: 10th International Conference on Laser-Assisted Micro- and Nanotechnologies
Серия: PROCEEDINGS OF THE SOCIETY OF PHOTO-OPTICAL INSTRUMENTATION ENGINEERS (SPIE)
Том: 5399
Год издания: 2004
Издательство: SPIE
Местоположение издательства: Bellingham, WA, United States
Первая страница: 179
Последняя страница: 183
DOI: 10.1117/12.552819
Аннотация: The possibility of the pulse laser radiation treatment of thin metal films on glass substrates has been studied experimentally. On the glass substrates with sprayed coating the diffraction structures were obtained due to the selective evaporation of metal at the interference of the powerful pulse laser radiation. The experiments were conducted using copper, aluminum films and films from titanium oxides. The thickness of the films on the glass substrates was 0.1divided by0.12 mum. The regimes normally used during the film, treatment with a laser beam were as follows: the wavelength was 1.06 mum, the pulse duration was 10 ns, and the energy density of the beam was 10 mJ/mm(2). To obtain an interference pattern on the treated surface the beam of the coherent radiation was preliminary split into two. In dependence on the convergence angle of the interference beams, the diffraction gratings had the lattice spacing in the range of 1divided by6 mum. They were used to produce diffraction lenses. These lenses are a plane device with a ring-shape zone of concentric grating grooves capable to focus a certain part of incident radiation. In dependence on the wavelength, the radiation is collected on the optic axis at different distances from the diffraction lens. This fact makes it possible to use the lens in production of a simple monochromator. The structure of the diffraction gratings obtained has been studied, and their main characteristics and main spheres of their application have been determined.
Добавил в систему: Зонов Руслан Геннадьевич

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

Интеллектуальная Система Тематического Исследования НАукометрических данных

The pulse laser processing of metal thin films on glass substratesстатья Исследовательская статья Тезисы

Прикрепленные файлы