Дата последнего поиска статьи во внешних источниках: 26 декабря 2018 г.

Работа с статьей


[1] The effect of phosphate melt cooling rate on phase composition and leach resistance of final waste form / K. V. Martynov, E. V. Zakharova, S. V. Stefanovsky, B. F. Myasoedov // MRS Advances. — 2018. — Vol. 3, no. 20. — P. 1085–1091. Slow cooling of phosphate melt at liquid nuclear waste solidification yields glass-crystalline material. Partial crystallization during melt solidification results in elemental partitioning among crystalline phase and glass: Al, Cr, Fe are concentrated in the crystalline phosphate phase while Ca, Ni, La, U enter predominantly in the residual glass. Glass dissolution rate and leach rate of La and U as rare earth and actinide surrogates depends strongly on the glass composition, for example reduction of Al2O3 content in the glass to ∼10-12 wt.% increases leachability by three orders of magnitude as compared to the glass with specified composition (∼18-22 wt.% Al2O3). [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть