Effect of absorbed hydrogen on active dissolution of carbon steel in near-neutral pH electrolyteстатья
Информация о цитировании статьи получена из
Scopus
Дата последнего поиска статьи во внешних источниках: 24 апреля 2018 г.
-
Авторы:
Nenasheva T.A.,
Marshakov A.I.
-
Журнал:
Journal of Corrosion Science and Engineering
-
Том:
16
-
Год издания:
2013
-
Первая страница:
1
-
Последняя страница:
12
-
Аннотация:
The dissolution kinetics of hydrogen-charged carbon steel in environments simulating the electrolyte under a delaminated coating on underground pipelines has been studied. It has been shown that the active dissolution of iron is considerably accelerated by hydrogen absorption by the metal. This effect can result in local corrosion, in particular, stress corrosion cracking of steel structures. © 2013 University of Manchester and the authors.
-