On the isomorphous phase transformation in the solid f.c.c. solutions Co-H at high pressuresстатья
Информация о цитировании статьи получена из
Scopus,
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 3 февраля 2015 г.
Аннотация:Samples of Co containing 0.2 at.% Fe and consisting of a mixture of approximately equal amounts of the h.c.p. (stable) and f.c.c. (metastable) phases were loaded with hydrogen by a 24 h exposure to a hydrogen atmosphere at 325 degrees C and pressures up to 9 GPa. X-ray diffraction at ambient pressure and 100 K has revealed a steep increase in the lattice parameter of the f.c.c. phase in the samples hydrogenated at 4-6 GPa, corresponding to an increase in the hydrogen content from few atomic per cent to an H/Co atomic ratio of approximately 0.95. This behaviour is interpreted as a supercritical anomaly of an isomorphous phase transformation in the f.c.c. solid solutions. The topology of the T-P phase diagram of the Co-H system is discussed in view of these observations.