Structure and crystallization of potassium titanium phosphate glasses containing B2O3 and SiO2статья Исследовательская статья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 23 ноября 2017 г.
- Авторы: Aronne A., Depero L.E., Sigaev V.N., Pernice P., Bontempi E., Akimova O.V., Fanelli E.
- Журнал: Journal of Non-Crystalline Solids
- Том: 324
- Номер: 3
- Год издания: 2003
- Издательство: Elsevier BV
- Местоположение издательства: Netherlands
- Первая страница: 208
- Последняя страница: 219
- DOI: 10.1016/S0022-3093(03)00263-1
- Аннотация: Transparent glasses composition of which can be expressed by the formula: (100-x)·(K2O·2TiO2·P2O 5)·x(K2O·2B2O3· 7SiO2), where x=5, 10, 15 and 20 mol% (KTP-xKBS), were obtained by melt quenching technique. The structure and crystallization behavior of these glasses have been examined by Fourier transform infrared spectroscopy, differential thermal analysis and X-ray diffraction. In spite of their nominal composition, the studied glasses exhibit a similar oxygen polyhedra distribution. However, significant differences were found in the trigonal BO3 units amount. During DTA runs all the examined glasses devitrify in two steps. In the former, very small crystals of an unknown crystalline phase are produced. In KTP-5KBS and KTP-10KBS glasses anatase phase was also detected. Attempts were made in order to identify the unknown phase (UTP) for which a AB3(XO4)2(OH)6 Crandallite-type structure was proposed where the A, B and X sites were occupied by K, Ti and/or Al, and P, respectively. In the second devitrification step the crystallization of the KTiOPO4 phase occurs while the UTP phase previously formed disappears. Isothermal heat treatments performed at temperature just above Tg have allowed one to obtain transparent crystal-glass nanocomposites, formed by crystalline nanostructure of the UTP phase uniformly dispersed in the amorphous matrix. © 2003 Elsevier B.V. All rights reserved.