Pinning Properties of PLD-Obtained GdBa2Cu3O7 −x Coated Conductors Doped With BaSnO3статья

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 19 октября 2017 г.

Работа с статьей

[1] Pinning properties of pld-obtained gdba2cu3o7 −x coated conductors doped with basno3 / V. Chepikov, N. Mineev, D. Abin et al. // IEEE Transactions on Applied Superconductivity. — 2017. — Vol. 27, no. 4. — P. 8000905–8000905. This work is devoted to high-rate pulsed laser deposition of BaSnO3 -doped superconducting films on long buffered metal tape substrates with the use of pilot-scale equipment and common deposition conditions typical for commercial 2G hightemperature superconducting wire production at SuperOx Japan. BaSnO3 inclusions were found to grow as nanocolumns elongated along the vertical direction and having biaxial texture. With BaSnO3 doping, the angular dependence of critical current measured at 77 K became much more isotropic. At 77 K, the liftfactor ( Ic /Ic sf) values in BaSnO3 doped samples increased almost twice in 0.5–3 T magnetic field in perpendicular orientation; at the same time, the absolute critical current increased only by 10%. At 4.2 K, in 0.5–3 T perpendicular field, the absolute critical current in doped samples increased 1.8 times. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть