Synthesis of Sm26Co11Ga6-type R26Co5+xIn12-x compounds (R––Y, Dy–Tm) (x = 0–0.2) and magnetic properties of Tb26Co5In12

Wenbin, S.; Garshev, A.V.; Yapaskurt, V.O.; Jinlei, Y.; Morozkin, A.V.

Авторы: Wenbin Shi, Garshev A.V., Yapaskurt V.O., Jinlei Yao, Morozkin A.V.
Журнал: Journal of Solid State Chemistry
Том: 347
Год издания: 2025
Издательство: Elsevier B.V.
Местоположение издательства: Netherlands
Первая страница: 125343-1
Последняя страница: 125343-7
Номер статьи: 125343
DOI: 10.1016/j.jssc.2025.125343
Аннотация: Ternary rare-earth-based R26Co5-6In12-11 (R = Y, Tb-Tm) compounds have been prepared by arc melting and subsequent annealing at 870 K. The powder X-ray diffraction analysis reveals that the samples crystallizes in the tetragonal Sm26Co11Ga6-type structure (space group P4/mbm, N 127, tP86). The lattice parameters follow the lanthanide contraction rule, decreasing from a = 1.19413 nm and c = 1.58441 nm of Tb26Co5In12 to a = 1.17353 nm and c = 1.56770 nm of Tm26Co5.2In11.8. Tb26Co5In12 is ferromagnetic with the Curie temperature TC = 72 K, and it shows two mixed ferro-antiferromagnetic ordering at Tm' ~ 66 K and Tm = 18 K, respectively. Tb26Co5In12 displays distinct hard magnet properties, e.g., the coercive field of 18 kOe, the saturation magnetisation of 166 mB/fu and the theoretical maximum energy product (BH)max of ~314 kJ/m3 at 2 K. The magnetocaloric effect of polycrystalline Tb26Co5In12 has been investigated using magnetic and heat capacity measurements.
Добавил в систему: Морозкин Александр Владимирович

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

Интеллектуальная Система Тематического Исследования НАукометрических данных

Synthesis of Sm26Co11Ga6-type R26Co5+xIn12-x compounds (R––Y, Dy–Tm) (x = 0–0.2) and magnetic properties of Tb26Co5In12статья Исследовательская статья

Прикрепленные файлы