Near surface modification of R-sapphire exposed to long term RF hydrogen-neon plasma

Авторы: Gorodetsky A.E., Markin A.V., Bukhovets V.L., Rybkina T.V., Zalavutdinov R.Kh, Zakharov A.P., Mukhin E.E., Razdobarin A.G.
Журнал: Technical Physics Letters
Том: 50
Номер: 11
Год издания: 2024
Издательство: Pleiades Publishing, Ltd
Местоположение издательства: Road Town, United Kingdom
Первая страница: 12
Последняя страница: 15
Оригинальные версии: Структурные изменения в поверхностных слоях сапфира при длительной экспозиции в высокочастотном разряде в смеси H2-Ne
DOI: 10.61011/0000000000
Аннотация: Samples of R-sapphire were exposed to long term RF hydrogen-neon plasma. Modification of near-surface layers was studied by XRD and XPS, and optical changes were assessed by spectrophotometry. After removing 270 nm thick layer the internal stresses remained at an initial value, but in the layer that probing by XRD individual blocks turned around and shifted from the Bragg reflection. XPS shows that aluminum is still an Al2O3 compound. Light transmission in the wavelength range 400−1000 nm remained unchanged which makes it possible to use sapphire as a protection window for optical diagnostics in fusion facilities.
Добавил в систему: Буховец Валентин Леонидович

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА