New scandium rhodium boride Sc4Rh17B12 with a framework structure: synthesis, crystal structure, and propertiesстатья

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.

Работа с статьей


[1] New scandium rhodium boride sc4rh17b12 with a framework structure: synthesis, crystal structure, and properties / A. M. Alekseeva, A. Leithe-Jasper, Y. Prots et al. // Russian Chemical Bulletin. — 2008. — Vol. 57, no. 3. — P. 532–540. The new scandium rhodium boride Sc4Rh17B12 was synthesized by arc-melting of the elements followed by annealing in inert atmosphere. The crystal structure of Sc4Rh17B12 was solved using single crystal X-ray diffraction data. The structure can be described as a three-dimensional framework formed by trigonal prisms [BRh6] and [BRh5Sc] with isolated boron atoms inside the prisms and trigonal prisms [BRh5B] representing the coordination polyhedra of paired boron atoms. The temperature dependences of the magnetic Susceptibility and specific resistance of Sc4Rh17B12 revealed that the compound is a Pauli paramagnet and shows metal-like specific resistance.

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть