Cold sintering of α and γ-modifications of aluminum oxohydroxides: A low-temperature route to porous corundum ceramics

Kholodkova, A.A.; Kornyushin, M.V.; Smirnov, A.V.; Arbanas, L.A.; Khrustalev, A.N.; Bazarova, V.E.; Shumyantsev, A.V.; Kupreenko, S.Y.; Ivakin, Y.D.

Авторы: Kholodkova A.A., Kornyushin M.V., Smirnov A.V., Arbanas L.A., Khrustalev A.N., Bazarova V.E., Shumyantsev A.V., Kupreenko S.Yu, Ivakin Yu D.
Журнал: Fine Chemical Technologies
Том: 19
Номер: 4
Год издания: 2024
Первая страница: 337
Последняя страница: 349
DOI: 10.32362/2410-6593-2024-19-4-337-349
Аннотация: Objectives. To obtain porous corundum ceramics using an innovative cold sintering process starting from different phase modifications of aluminum oxohydroxide—boehmite γ-AlOOH and diaspore α-AlOOH; to study the phase and structural properties of the resulting materials; and to assess their permeability to water. Results. Cold sintering enables the formation of single-phase corundum ceramics with an open porosity of 47.9% directly from the initial boehmite powder with the addition of 5 wt % corundum in the presence of 20 wt % water at a temperature of 450°C, mechanical pressureof 220 MPa, and isothermal exposure for 30 min. Under the same conditions of cold sintering, a mixture of diaspore and boehmite was transformed into α-AlOOH ceramics. This then turned into corundum with an open porosity of 39% when calcined in air at 600°C for1 h. The resulting materials had permeability for pure water above 5000 L/(m2∙h∙bar).Conclusions. Cold sintering is a promising approach to producing porous corundum ceramics which can be used in filtration systems. Compared to traditional ceramic technology, the new approach reduces energy, time, and labor costs in the material manufacturing. It also eliminates the need to use auxiliary substances (binders, pore-forming agents, etc.).
Добавил в систему: Купреенко Степан Юрьевич

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

Интеллектуальная Система Тематического Исследования НАукометрических данных

Cold sintering of α and γ-modifications of aluminum oxohydroxides: A low-temperature route to porous corundum ceramicsстатья Исследовательская статья

Прикрепленные файлы