Hafnia-yttria-alumina-silica based optical fibers with diminished mid-IR (>2 μm) lossстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 8 августа 2017 г.

Работа с статьей


[1] Hafnia-yttria-alumina-silica based optical fibers with diminished mid-ir (>2 μm) loss / A. V. Kir’yanov, S. H. Siddiki, Y. O. Barmenkov et al. // Optical Materials Express. — 2017. — Vol. 7, no. 7. — P. 2511–2518. Fabrication details and basic characteristics of a set of novel multimode hafniayttria- alumina-silicate (HYAS) core-glass based fibers, one of which is co-doped with bismuth (Bi), for the mid-IR (> 2 μm) spectral range are reported. It is demonstrated that fibers of this type possess low fundamental loss in the spectral range beyond 2 μm, lowered by fewer times as compared to conventional silica-based ones, even at moderate (units of mol.%) co-doping with hafnium. This makes them attractive for versatile mid-IR applications. Furthermore, HYAS core-glass fiber co-doped with Bi is revealed to have all the signs of ‘active’ (fluorescing) Bi-related centers, thus being suitable for lasing/amplifying in the near-IR spectral range. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть