Magnetic properties of Yb23Cu7Mg4-type {Gd, Tb}23Ni7In4 compounds

Авторы: Yizhou Cao, Knotko A.V., Yapaskurt V.O., Yang Hu, Jinlei Yao, Morozkin A.V.
Журнал: Journal of Solid State Chemistry
Том: 335
Год издания: 2024
Издательство: Elsevier B.V.
Местоположение издательства: Netherlands
Первая страница: 124706-1
Последняя страница: 124706-7
Номер статьи: 124706
DOI: 10.1016/j.jssc.2024.124706
Аннотация: The polycrystalline Yb23Cu7Mg4-type {Gd, Tb}23Ni7In4 compounds (space group P63/mmc, N 194, hP68) were prepared by arc melting with following annealing. They exhibit ferromagnetic ordering below Curie temperature TC = 142 K for Gd23Ni7In4 and TC = 112 K for Tb23Ni7In4, respectively. A field-sensitive antiferromagnetic transformation takes place around 90 K in Gd23Ni7In4 and 106 K in Tb26Ni7In4, respectively. Down to 10 K, they are soft ferromagnets with magnetizations of 4.7 mB/Gd for Gd23Ni7In4 and 5.7 mB/Tb for Tb23Ni7In4 in 90 kOe. In a field change of 50 kOe around TC, Gd23Ni7In4 shows magnetic entropy change of -4.7 J/kgK at 133-143 K, while Tb23Ni7In4 shows magnetic entropy change of -5.4 J/kgK at 109 K.
Добавил в систему: Морозкин Александр Владимирович

№	Имя	Описание	Имя файла	Размер	Добавлен
1.	ЗАКЛЮЧЕНИЕ о возможности открытого опубликования 14.05.2024 № 112.1000.2024		Заключение_112-1000-2024.pdf	365,4 КБ	3 апреля 2025 [morozkin]

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА