Formation of Bi-2212 phase and phase assemblage in Ga-doped BSCCO systemстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.

Работа с статьей

[1] Formation of bi-2212 phase and phase assemblage in ga-doped bscco system / P. E. Kazin, V. V. Poltavets, O. N. Poltavets et al. // Physica C: Superconductivity and its Applications. — 1999. — Vol. 324, no. 1. — P. 30–38. Phase relations in the Bi-Sr-Ca-Cu-Ga-O system were investigated at 850 degrees-900 degrees C. Two Ga-containing phases were found to be compatible with Bi-2212. Compositions of these phases were estimated as Bi(0.2)SF(1.8-x)Ca(x)Ga(2)O(z) and Bi(1.7)Sr(2.3)Ca(0.6)Cu(1.6)Ga(0.4)O(z). The Ga content in Bi-2212 was limited to 15-25 mol%. The mixture of Bi-2212 with the Ga-containing phases started to melt around 870 degrees C, and at 890 degrees C yields liquid and (Sr, Ca)(3)Ga(2)O(6) phase. The superconducting composites Bi-2212/Bi(0.2)Sr(1.8-x)Ca(x)Ga(2)O(z) were prepared using partial melting procedure. The dopant had only a slight effect on T(c), the flux pinning in the material was not improved at all. (C) 1999 Elsevier Science B.V. All rights reserved. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть