Glass-ceramic composites with strontium hexaferrite ultrafine particles in the SrO-Fe2O3-B2O3-SiO2 systemстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.

Работа с статьей


[1] Glass-ceramic composites with strontium hexaferrite ultrafine particles in the sro-fe2o3-b2o3-sio2 system / D. D. Zaitsev, E. A. Gravchikova, P. E. Kazin et al. // International Journal of Applied Ceramic Technology. — 2006. — Vol. 3, no. 4. — P. 279–283. Glass samples with nominal compositions SrFe12O19+(12-n)SrB2O4+nSrSiO(3), n=3, 6, 9 were prepared by rapid quenching of the melt. Processes of glass devitrification were studied. The samples were annealed at temperatures of 600-900 degrees C, and the resulting glass-ceramics was characterized by XRD, SEM, EDX, and magnetic measurements. SrFe12O19 crystallizes above 700 degrees C and forms nano- and submicron platelet particles with the aspect ratio depending on the thermal treatment conditions. The glass-ceramic samples annealed at 900 degrees C show coercive force values in the range of 422-455 kA/m. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть