Viscosity of liquid Al-Co alloys with a cobalt content up to 15 at %статья

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 26 апреля 2017 г.

Работа с статьей


[1] Viscosity of liquid al-co alloys with a cobalt content up to 15 at % / A. L. Bel'tyukov, S. G. Men'shikova, V. I. Lad'yanov, A. Y. Korepanov // High Temperature. — 2016. — Vol. 54, no. 5. — P. 667–674. By means of the torsional vibrations method, the temperature dependences (from the liquidus up to 1200A degrees C) of the kinematic viscosity of liquid aluminum and Al-Co melts with a cobalt content up to 15 at % were obtained. For all the liquid alloys investigated, the temperature dependences of the viscosity obtained in the heating and cooling regimes coincide. The temperature dependences were approximated by the Arrhenius equation. For liquid aluminum and melts with a cobalt content below 1.4 at % inclusive, a viscosity polytherm deviation from the Arrhenius dependence was discovered. The viscosity dependences on the concentration at a fixed temperature and the activation energy of the viscous flow were plotted. An increase in the cobalt content in the melt results in an increase in the viscosity and the activation energy of the viscous flow values. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть