Experimental Investigation and Thermodynamic Modelling of Ag–In–Pd Ternary Systemстатья
- Авторы: Pavlenko A.S., Ptashkina E.A., Zhmurko G.P., Kabanova E.G., Kareva M.A., Khoroshilov A.V., Kuznetsov V.N.
- Журнал: Russian Journal of Physical Chemistry A
- Том: 97
- Номер: 1
- Год издания: 2023
- Издательство: Pleiades Publishing, Ltd
- Местоположение издательства: Road Town, United Kingdom
- Первая страница: 42
- Последняя страница: 49
- DOI: 10.1134/S0036024423010235
- Аннотация: Phase equilibria in Ag–In–Pd ternary system were studied using Scanning electron microscopy,Energy-dispersive X-ray spectroscopy (EDX) and X-Ray diffraction method (XRD). The solubilities of thethird components in Ag–In and In–Pd binary phases were established, as well as composition ranges (from 4 to 17.5 at % Ag at 25 at % In) and crystal structure of τ ternary compound (Al3Ti). New thermodynamic assessment of Ag–In–Pd ternary system was performed, basing on the published experimental data and those obtained in the present work. Good agreement was achieved between the calculation results and the experimental data on phase equilibria and thermodynamic properties of the phases. The results of the calculation reproduce well experimental DTA/DSC data of three samples (the data were not included into the optimization). This additionally supports the correctness of the obtained thermodynamic description.