Crystal growth of the neodymium-rich Nd1+xBa2-xCu3Oz solid solutionстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:In the present work on the basis of experimental phase relations in the copper-rich corner of the Nd-Ba-Cu-O system, the insulating Nd1+xBa2-xCu3Oz solid solution single crystals, with x = 0.43-0.85, were grown by the top-seeded-solution-growth method. The as-grown Nd1.85Ba1.15Cu3Oz crystals were found to be orthorhombic. As a result, the twin-like structure was observed and the twin-plane re-entrant-edge (TPRE) crystal growth mechanism was proposed. (C) 1998 Elsevier Science S.A. All rights reserved.