Luminescence of MgF2-WO3 ceramics synthesized in the flux of 1.5 MeV electron beamстатья
- Авторы: Lisitsyna Liudmila A., Popov Anatoli I., Karipbayev Zhakyp T., Mussakhanov Dossymkhan A., Feldbach Eduard
- Журнал: Optical Materials
- Том: 133
- Год издания: 2022
- Издательство: Elsevier BV
- Местоположение издательства: Netherlands
- Первая страница: 112999
- DOI: 10.1016/j.optmat.2022.112999
- Аннотация: The results of comparative analysis of optical properties of MgF2 single crystals and MgF2 ceramics, non-doped and doped with tungsten trioxide obtained in the process of high-speed radiation synthesis in air under a flux of 1.5 МеV electrons, are presented.The synthesized ceramics are found to have a high degree of crystallinity, their elements composition is close to stoichiometric, and the phase composition is a rutile lattice.Using time-resolved spectroscopy, it was shown that the initial defectiveness of as-synthesized ceramics samples is represented by emission centers belonging to WO3 complexes and radiation defects of F2- types with spectral-kinetics parameters similar to those in irradiated by ionizing radiation MgF2 single crystals. The ratio between these types of defects is determined by the temperature and luminescence excitation method and the ratios between dopant and co-dopant (LiOH).In MgF2 ceramics samples, being exposed to ionizing radiation, two radiative channels of relaxation of electronic excitations were found: T-So (triplet-singlet) emission transition in self-trapped excitons (STE) at 3.2 eV and recombination of F–H Frenkel pairs accompanied with the emission at 4.0 eV. The temperature dependences of these channel efficiency in the range of 5–300 K are similar to those ones observed in MgF2 single crystals.
- Добавил в систему: Попов (Popov) Анатолий (Anatoli) Иванович
Прикрепленные файлы
| № | Имя | Описание | Имя файла | Размер | Добавлен |
|---|---|---|---|---|---|
| 1. | Полный текст | MgF2_WO3_2022.pdf | 3,1 МБ | 21 ноября 2022 [popov@latnet.lv] |