Nanocomposites Based on Polyepoxyurethane-Containing Isocyanurate Binders

Авторы: Keimakh M.D., Kravchenko T.P., Shishkinskaya V.A., Askadskii A.A., Gorbunova I.Yu
Журнал: Polymer Science - Series D
Том: 15
Номер: 4
Год издания: 2022
Издательство: Springer Verlag
Местоположение издательства: Germany
Первая страница: 499
Последняя страница: 502
Оригинальные версии: НАНОКОМПОЗИТЫ НА ОСНОВЕ ПОЛИЭПОКСИУРЕТАНСОДЕРЖАЩИХ ИЗОЦИАНУРАТНЫХ СВЯЗУЮЩИХ
DOI: 10.1134/S1995421222040128
Аннотация: The application of carbon nanoparticles as modifiers of polyepoxyurethane-containing isocyanurates results in achieving the highest increase in physicochemical properties even when they have a low content in the composition. Impact number A at nanocarbon weight content W of 0.5% is almost 1.5 times higher than that of the matrix polymer. The obtained dependence of the impact number on the weight content A = (W) for the considered nanocomposite samples has an extremum pattern, where the maximum is achieved at W = 0.5%. At W = 0.5%, elasticity modulus Ecomp of the composite (in compression tests) increased almost 1.3-fold compared to the starting polymer.
Добавил в систему: Аскадский Андрей Александрович

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА