Lithium diffusion in a new cathode material Li0.8[Ni0.6Sb0.4]O2 studied by 7Li NMRстатья

Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 12 июля 2017 г.

Работа с статьей


[1] Lithium diffusion in a new cathode material li0.8[ni0.6sb0.4]o2 studied by 7li nmr / T. Salikhov, E. Klysheva, E. Zvereva et al. // Magnetic Resonance in Solids. — 2016. — Vol. 18. — P. 16207. A rhombohedral layered α-NaFeO2-type compound, Lix[Ni(1+x)/3Sb(2-x)/3]O2 (x=0.8) has been prepared from the sodium analogue by ion exchange at 570 K. In contrast to the stoichiometric composition Li3Ni2SbO6, it shows considerable Li/Ni inversion and no long-range Ni/Sb ordering. The temperature dependence of the 7Li NMR spin-lattice relaxation rate and linewidth data measured at temperature range from 30-450 K show the sharp increase of lithium ions mobility comparing to the stoichiometric compound Li3Ni2SbO6. From the NMR data the activation energy was estimated by different methods. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть