Impact Strength of 16Cr-20Ni-2Mo-Ti Austenite Steel under Shockwave Load in Sub-Microsecond Rangeстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 мая 2022 г.
Аннотация:The paper focuses on the measurements of the free surface displacement of 16Cr-20Ni-2Mo-Ti reactor vessel steel specimens at room temperatures and higher. It is shown that the mechanical inhomogeneity of the steel structure leads to a significant spread in values of the Hugoniot elastic limit and spallation strength. The experiments show that the high-pressure hexagonal close packed structure does not appear after the steel specimen compression.