Formation of wear-resistant graphite/diamond-like carbon nanocomposite coatings on Ti using accelerated C60-ionsстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 26 января 2022 г.
- Авторы: Khadem Mahdi, Pukha Vladimir E., Penkov Oleksiy V., Khodos Igor I., Belmesov Andrei A., Nechaev Grigory V., Kabachkov Evgeniy N., Karaseov Platon A., Kim Dae-Eun
- Журнал: Surface and Coatings Technology
- Том: 424
- Год издания: 2021
- Издательство: Elsevier BV
- Местоположение издательства: Netherlands
- Первая страница: 127670
- DOI: 10.1016/j.surfcoat.2021.127670
- Аннотация: The nanostructural and tribological characteristics of carbon nanocomposite coatings (CNCs), deposited by accelerated C60 ions at high temperatures, were studied. The CNCs were successfully fabricated on Ti-alloy using a flux that contained C60 ions with 5 and 10 keV energies. Unlike the previous studies, ion mass-separator was not implemented to the deposition process. This enabled deposition of sp2-rich CNCs with a lower coefficient of friction (COF) at a higher deposition rate. Laser confocal microscopy, atomic force microscopy transmission electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, and X-ray Auger Electron Spectroscopy were used to investigate the structure of the coatings and friction test results. A carbon nanocomposite film consisting of graphite nanocrystals enclosed in an amorphous diamond-like matrix was formed at a deposition temperature of 300–400 °C. Upon deposition of the CNC, a COF of ~0.06 was achieved, which was almost one order of magnitude lower than that of bare Ti-alloy substrate. The surface wear was reduced by 360 times. The wear mechanism was changed from abrasive wear (on bare Ti-alloy) to a burnishing smoothening of the surface roughness (on CNCs). The transfer of graphite nanocrystals from the coating to the counter surface was identified and observed to act as a solid lubricant.