Structural and electrochemical properties of Li1+xNi0.5Mn0.5O2+delta (0 <= x <= 0.7) cathode materials for lithium-ion batteriesстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.

Работа с статьей


[1] Structural and electrochemical properties of li1+xni0.5mn0.5o2+delta (0 <= x <= 0.7) cathode materials for lithium-ion batteries / S. H. Choi, O. A. Shlyakhtin, J. Kim, Y. S. Yoon // Journal of Power Sources. — 2005. — Vol. 140, no. 2. — P. 355–360. A comparative analysis of the properties of LiNi0.5Mn0.50O2 and Li1-xNi0.5Mn0.5O2 (0.2 less than or equal to x less than or equal to 0.7) powders, obtained by the freeze drying method, was performed. Lattice parameters of Li1+xNi0.5Mn0.5O2 decreased considerably with growing amounts of Li until x = 0.3: at x > 0.5 trace amounts of Li2MnO3 are observed by X-ray diffraction (XRD) patterns. X-ray photoelectron spectroscopy (XPS) analysis displayed an increase of Ni3+/Ni2+ ratio at 0.3 < x < 0.5, while Mn 2p spectra were almost identical in all samples. Rechargeable capacity values (V = 2.5-4.6 V) increased systematically with x reaching its maximum (185-190 mAh g(-1)) at x = 0.5. Samples with supersioichiometric lithium content also demonstrated good C rate characteristics. (C) 2004 Elsevier B.V. All fights reserved. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть