Effect of the cation on the phase composition of nanocrystalline dioxides of the titanium family synthesized by hydrothermal treatment of amorphous hydroxide gelsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The phase composition of TiO2, ZrO2, and HfO2 nanopowders manufactured by hydrothermal treatment of amorphous hydroxide gels at T = 523 K and the saturated water vapor pressure (for tau from 10 min to 24 h) or at high pressures of 3.0 or 4.0 GPa (T = 523 K, T = 30 min) is considered in relation to the physicochemical properties of the powders. The samples synthesized are characterized using X-ray powder diffraction, X-ray line broadening analysis (XLB), thermogravimetry, and electron microscopy (SEM and TEM). The BET specific surface areas are determined using nitrogen capillary adsorption. The nature of the cation is shown to affect the phase composition of the nanosized dioxides of the titanium family.