Behavior of magnetization in high magnetic fields of (Sm,Ho)2Fe17N2.4 powders obtained by mechanical grindingстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 4 июня 2021 г.
Аннотация:Fundamental magnetic properties of the R2Fe17 compounds are highly sensitive to the atomic substitutions and interstitial absorption of light elements (nitrogen or hydrogen). In our work, both were combined, and the influence of the substitutions in the R-sublattice and nitrogen absorption on the magnetization behavior of Sm2Fe17 compound in magnetic fields up to 58 T was studied. (Sm,Ho)2Fe17N2.4 nitride was prepared. Magnetisation measurements were carried out on powder samples. Nanopowders of (Sm,Ho)2Fe17N2.4 were obtained by mechanical grinding. The grinding time was varied from 0 to 60 minutes. The strength of the inter-sublattice coupling in all samples is estimated by analyzing high-field magnetization data. In our work is shown that nitrogenation weakens the inter-sublattice exchange interaction in the compounds up to 45 - 50 %. Grinding time and, as a consequence, particle size affects theinter-sublattice exchange interaction. To achieve a ferromagnetic state, fields are needed wellin excess of 58 T.