Neutron scattering studies of the structure and lattice dynamics of a solid solution of hydrogen in alpha manganeseстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.

Работа с статьей


[1] Neutron scattering studies of the structure and lattice dynamics of a solid solution of hydrogen in alpha manganese / V. K. Fedotov, V. E. Antonov, K. Cornell et al. // Journal of Physics Condensed Matter. — 1998. — Vol. 10, no. 24. — P. 5255–5266. A solid solution of hydrogen in alpha-Mn, alpha-MnHx with x = 0.073, was prepared at 623 K and a hydrogen pressure of 0.85 GPa. A profile analysis of the neutron diffraction patterns measured at 225 K and at 300 K showed that hydrogen in alpha-MnH0.073 randomly occupies the interstitial positions 12e (0, 0, 0.538) of the alpha-Mn host lattice. An inelastic neutron scattering study of alpha-MnH0.073 at 90 K revealed a pronounced peak at 6.4 meV and a rather broad optical hydrogen band with peaks at 73, 105 and 123 meV. The splitting of the optical band into three different modes agrees with the low symmetry, 2, of the 12e hydrogen sites. A tentative interpretation is given for the peak at 6.4 meV. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть