21R-Sialon ceramics, obtained by hot pressingстатья
Информация о цитировании статьи получена из
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 28 октября 2020 г.
Аннотация:The formation, densification behaviour and mechanical properties of 21R polytype were studied. Self-propagating high-temperature synthesis obtained the starting powder of 21R-sialon. Sealing was carried out by hot pressing in the temperature range 1650-1800°C. With increasing temperature, there is an increase in density and mechanical properties.