Influence of macro- and microcomponent content on the color of M2O—PbO—SiO2 (M = Li, Na, K, Rb, Cs) glasses doped with copper

Информация о цитировании статьи получена из Web of Science, Scopus
Дата последнего поиска статьи во внешних источниках: 3 июня 2020 г.

Авторы: Andreev M.N., Ratnikov D.S., Dolzhenko V.D., Belousov Yu A., Drozdov A.A.
Журнал: Russian Chemical Bulletin, Int. Ed
Том: 69
Номер: 4
Год издания: 2020
Первая страница: 697
Последняя страница: 703
DOI: 10.1007/s11172-020-2820-9
Аннотация: The dependence of lead silicate glass color, applied using copper(II) ions, on lead content in the glass, the nature of the alkali metal, and copper content was studied. It was shown that the principal contribution to the color is made by the shift of the fundamental absorption edge, which correlates with the amount of lead and copper ions. According to EPR results for glasses with the studied compositions, copper ions have a tetragonally distorted octahedral coordination environment, which does not change considerably with composition. The CuII d—d-transition bands also do not undergo considerable changes.
Добавил в систему: Андреев Максим Николаевич

	ИСТИНА	Войти в систему Регистрация
	Интеллектуальная Система Тематического Исследования НАукометрических данных
	Главная Поиск Статистика О проекте Помощь

ИСТИНА