A new green-to-transmissive polymer with electroactive PEDOT: PSS as an interface layer for achieving high-performance electrochromic deviceстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 1 февраля 2021 г.
Авторы:
Lv X.,
Bi Q.,
Tameev A.,
Zhang Y.,
Qian L.,
Ouyang M.,
Zhang C.
Аннотация:A new neutral green electrochromic (EC) polymer, namely poly(5,8-bis(2,3-dihydro[3,4-B][1,4]dioxin-5-yl)-2,3-dual(4-(hexadecyloxy) phenyl) quinoxaline) (PBOPEQ) was designed and synthesized. PBOPEQ-poly(3,4-ethylene dioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) film was further prepared by electrochemical polymerization on the PEDOT:PSS modified indium tin oxide (ITO) electrode. Scanning electron microscopy images and ultrasonic experiment indicate that PBOPEQ-PEDOT:PSS film shows better film-forming ability and stronger interface adhesive with ITO electrode compared to that of PBOPEQ film. It is worth mentioning that PBOPEQ-PEDOT:PSS film presents more reversible redox characteristic, better optical contrast (~40%) and coloration efficiency (~230 cm(2) C-1) at 678 nm, excellent EC stability and memory property (36 hr), which should be ascribed to that the electroactive PEDOT:PSS layer facilitates the charge transfer process and enhances the ion doping/dedoping properties. EC device based on PBOPEQ-PEDOT:PSS film exhibits superior integrated performance such as reversible color change from green to transmissive, optical contrast of 41.0% and switching time less than 1 s. Accordingly, PBOPEQ-PEDOT:PSS is an excellent EC material when combined with electroactive PEDOT:PSS interface layer for achieving high performance device, which shows potential applications in displays, electronic papers, and tags.