Mutual transformation between crystalline phases in silicon after treatment in a planetary mill. HRTEM studiesстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 4 декабря 2016 г.

Работа с статьей


[1] Mutual transformation between crystalline phases in silicon after treatment in a planetary mill. hrtem studies / K. Boris, A. Mikhail, P. Igor et al. // Acta Crystallographica Section B: Structural Science, Crystal Engineering and Materials. — 2016. — Vol. 72. — P. 733–737. High-resolution transmission electron microscopy (HRTEM) studies of silicon after treatment in a planetary mill have been performed. It is shown that along with the initial phase of silicon, Si-I, the sample also contains some high-pressure phases: Si-III (Kasper phase) and Si-IV (lonsdaleite).We studied the orientation relationship between the particles of different phases, finding that there are, in general, two mechanisms of formation of Si-IV: (1) through the stacking faults formation; (2) through the transformation first to the Kasper phase (Si-III), and then from the Kasper phase to Si-IV. Estimations of temperature and pressure conditions in the planetary ball mill made previously are in accordance with the conditions of formation of the above-mentioned phases. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть