Bone cements in the calcium phosphate-calcium sulfate systemстатья

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 26 августа 2016 г.

Работа с статьей


[1] Bone cements in the calcium phosphate-calcium sulfate system / V. V. Smirnov, O. S. Antonova, M. A. Goldberg et al. // Doklady Chemistry. — 2016. — Vol. 467. — P. 136–139. Cement materials in the calcium phosphate-calcium sulfate system were proposed for bone tissue reconstruction. Mixtures of calcium sulfate and amorphous calcium sulfate in the weight ratios 20: 80, 40: 60, 60: 40, and 80: 20 were used as a cement flour, and an acidic solution of orthophosphoric acid was used as a setting liquid. Cement materials based on dicalcium phosphate dihydrate and calcium sulfate were obtained, and the phase composition, setting time, compressive strength, and microstructure of cements were studied. A phenomenon of dispersion strengthening of cements by adding 20 wt % calcium sulfate was detected. The obtained cement stone had a strength to 60 MPa, a setting time of 6-7 min, and uniform microstructure with a crystal size of 1-2 mu m. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть