High–temperature crystallization of novel rare–earth borate materials: single crystals and thin filmsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 19 июля 2013 г.
Аннотация:Phase formation has been studied in the complex system
YbAl3(BO3)4 - K2Mo3O10 - B2O3 - Yb2O3 within the stability region of YbAl3(BO3)4 (YbAB).
The obtained data were compared with those for YAl3(BO3)4 as another end member of the
YbAB-YAB solid solutions. Visually transparent (Er,Yb):YAl3(BO3)4 single crystals with a
typical size up to 10×10×15 mm3 and crystalline layers were obtained from K2Mo3O10 based
fluxed melts. The 1.5 μm emission spectra of (Er,Yb):YAl3(BO3)4 thin films as well as bulk
crystals were measured using CW Ti:sapphire laser tuned to 976 nm as a pump source.