Study of degradation of Na2Тi3O7-based electrode during cyclingстатья

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 6 мая 2019 г.

Работа с статьей


[1] Study of degradation of na2Тi3o7-based electrode during cycling / T. L. Kulova, Y. O. Kudryashova, A. A. Kuz’mina и др. // Journal of Solid State Electrochemistry. — 2019. — Т. 23, № 2. — С. 455–463. The degradation of electrodes based on sodium titanate (Na2Ti3O7) was studied using the methods of galvanostatic cycling,cyclic voltammetry, Raman spectroscopy, and electrochemical impedance spectroscopy. It is established that during the cycling, there is splitting of sodium titanate intergrown plates and constant growth of solid electrolyte interface on the surface of Na2Ti3O7 particles. These factors account for the degradation of Na2Ti3O7 at cycling. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть