Phase equilibria in Cu-Al-Zr system at 1073 K and aluminum concentration of less than 55 at %статья

Информация о цитировании статьи получена из Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 4 февраля 2014 г.

Работа с статьей


[1] Phase equilibria in cu-al-zr system at 1073 k and aluminum concentration of less than 55 at % / K. B. Kalmykov, N. E. Dmitrieva, N. L. Zvereva et al. // Moscow University Chemistry Bulletin. — 2012. — Vol. 67, no. 4. — P. 171–176. X-ray diffraction and electron probe microanalysis were used to investigate phase equilibria in the ternary Cu-Al-Zr system at 1073 K in the Zr-rich region. The fragment of the isothermal section of the system was plotted. The regions of homogeneity of the ternary ZrCu 2Al and ZrCu xAl 2 - x phases were investigated. The type of phase equilibria between binary and ternary compounds of the Al-Cu-Zr system was established. It was found out that, at a Zr concentration above 55 at %, ternary compounds are not formed, and the Zr 3Al and Zr 2Cu phases were in equilibria with α-Zr at 1073 K. © 2012 Allerton Press, Inc. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть