Phase diagram and thermodynamic properties of phases in the In-Te systemстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The In-Te phase diagram was refined in the composition range 0 to 71.77 at.% Te; the phases In4Te3, InTe, In2Te3, and In2Te5 were found to exist. Vaporization of In2Te3 and InTe was studied by the mass spectrometric method and the rho (Te2)-T diagram was constructed. The standard molar enthalpies of formation of mentioned compounds were determined by direct synthesis calorimetry. The heat capacity of the solid In(2)Te3 was measured in a vacuum adiabatic calorimeter at 5 to 310 K, and the H degrees (T)-H degrees (0), S-T, and G degrees (T)-H degrees (0) functions were calculated.