Modification of Li[Li0.13Ni0.2Mn0.47Co0.2]O2 cathode material by layered CeO2–C coatingстатья

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 6 марта 2019 г.

Работа с статьей

[1] Modification of li[li0.13ni0.2mn0.47co0.2]o2 cathode material by layered ceo2–c coating / K. A. Kurilenko, O. A. Shlyakhtin, D. I. Petukhov et al. // Journal of Solid State Electrochemistry. — 2019. — Vol. 23. — P. 433–439. Li[Li0.13Ni0.2Mn0.47Co0.2]O2 (LLNMC) cathode materials coated with CeO2 and pyrolytic carbon have been obtained by the consecutive thermal decomposition of Ce(NO3)3 and polystyrene at the surface of LLNMC powder. EDX analysis combined with transmission electron microscopy revealed the uniform coating of LLNMC grains with nanosized ceria particles. The XPS spectra of LLNMC coated with CeO2 and carbon indicated a considerable amount of –С=С– bonds in the carbonized polystyrene pyrolysis products. The layered CeO2–C coating promotes a decrease in the electrode polarization and the charge transfer resistance of LLNMC during cycling, thus promoting a better rate capability of the cathode material. A combined effect of the CeO2 and carbon coatings results in the increase of the electrochemical capacity of LLNMC to 220 mAh g−1 at C/10. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть