[1] New lead vanadium phosphate with langbeinite-type structure: Pb1.5v2(po4)(3) / R. V. Shpanchenko, O. A. Lapshina, E. V. Antipov et al. // Materials Research Bulletin. — 2005. — Vol. 40, no. 9. — P. 1569–1576. The new lead vanadium phosphate Pb1.5V2(PO4)(3) was synthesized by solid state reaction and characterized by X-ray powder diffraction, electron microscopy, and magnetic susceptibility measurements. The crystal structure of Pb1.5V2(PO4)(3) (a=9.78182(8) angstrom, S.G. P2(1)3, Z=4) was determined from X-ray powder diffraction data and belongs to the langbeinite-type structures. It is formed by corner-linked V3+O6 octahedra and tetrahedral phosphate groups resulting in a three-dimensional framework. The lead atoms are situated in the structure interstices and only partially occupy their positions. An electron microscopy study confirmed the structure solution. Magnetic susceptibility measurements revealed Curie-Weiss (CW) behavior for Pb1.5V2(PO4)(3) at high temperature whereas at around 14 K an abrupt increase on the susceptibility was observed. (C) 2005 Elsevier Ltd. All rights reserved. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть