Manufacture of Magnesium Oxide Nanoparticles Coated with Silica Shellsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 10 декабря 2018 г.
Аннотация:MgO@SiO2 core–shell nanoparticles were manufactured, and a synthetic protocol was developed
to prepare MgO nanoparticles where the SiO2 shell thickness was less than 10 nm. The influence of synthesis parameters on the formation of MgO@SiO2 nanoparticles was studied. The fact of a SiO2 shell being formed on the MgO surface was established and the sizes of the thus-prepared MgO@SiO2 nanoparticles were determined by TEM and Fourier-transform IR spectroscopy.