Phase diagram of the Sb-Se-I system and thermodynamic properties of SbSeIстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:The Sb-Se-I system was investigated by using the DTA and XRD analyses and EMF measurements with an antimony electrode. The T-x diagram of the binary Sb-I system was accurately redefined. A number of polythermal sections and the projection of the liquidus surface were constructed. The fields of the primary crystallization, as well as the types and coordinates of non- and monovariant equilibria were determined. It is shown that the quasi-binary sections Sb(2)Se(3)-SbI(3), Sb-SbSeI, SbI(3)-Se, and SbSeI-Se triangulate the Sb-Se-I system, leading to five independent subsystems. A broad area of immiscibility, that overlaps a certain part of the antimony primary crystallization field, was found. From the EMF measurements, the partial molar functions of antimony (Delta(G) over bar, Delta(H) over bar, Delta(S) over bar) as well as standard integral thermodynamic functions of SbSeI were calculated. The latter were found to have the following values: Delta G(f.298)(0) = 80.12 +/- 1.81 kJ/mol; Delta H(f.298)(0) = 77.3 +/- 1.8 kJ/mol; S(298)(0) = 155.2 +/- 9.5 J/(mol K). (C) 2010 Elsevier B.V. All rights reserved.