BI-2201 PHASES - SYNTHESIS, STRUCTURES AND SUPERCONDUCTING PROPERTIESстатья
Информация о цитировании статьи получена из
Scopus,
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 9 ноября 2013 г.
Аннотация:The Bi2+xSr2-xCuO6+delta (Bi-2201) phases and La substituted Bi-2201 compounds with general formulas Bi2Sr2-xLaxCuO6+delta and Bi23-xSr1.7LaxCuO6+delta were prepared and characterized by X-ray powder diffraction, electron diffraction, iodometric titration and resistance measurements. The monophasic samples of Bi2+xSr2-xCuO6+delta were obtained in air at 850 degrees C for 0.15 less than or equal to x less than or equal to 0.4; while synthesis at 740 degrees C in oxygen flow extended this range to the stoichiometric cation composition (0 less than or equal to x less than or equal to 0.4). The superconducting transitions were not detected for these monophasic samples in contrast to the La substituted phases which exhibited superconductivity, and the highest T-c,T-onset = 33 K was found for the Bi2Sr1.6La0.4CuO(6.33) compound. Superconductivity in the Bi2Sr2-xLaxCuO6+delta series exists in overdoped and underdoped regions. Incommensurately modulated structures of nonsuperconducting Bi2.3Sr1.7CuO6.23 phase and superconducting Bi2Sr1.7La0.3CuO6.28 phase (T-c,T-onset = 26 K) were refined from X-ray powder data by a Rietveld technique using the four-dimensional space group P:A2/a:-11. The maximal Cu displacements from the average position in the first structure was found to be sufficiently larger than in the latter one. The distorted structural arrangement of the (CuO2) layers in the Bi2.3Sr1.7CuO6.23 structure can be a reason for the suppression of superconductivity in this phase, while their less corrugated configuration in the La containing Bi-2201 structure leads to the existence of superconductivity.