Magnetostriction and magnetic anisotropy in TbFe11TiHx (x=0, 1) single crystalsстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.
Аннотация:Single crystals of TbFe11Ti and its hydride with tetragonal ThMn 12-type structure were obtained. Magnetostriction measurements have been made on TbFe11TiHx (x=0, 1) single crystals by the applied strain gauge method in the temperature range from 77 to 400 K and in magnetic fields up to 13 kOe. Magnetization measurement along the main crystallographic directions of the tetragonal structure have been performed on RFe11TiHx (x=0, 1) single crystals in applied high magnetic fields up to 120 kOe in the temperature range from 4.2 to 300 K. It was concluded that hydrogenation results in an increase in rare-earth anisotropy that leads to the disappearance of the spin-reorientation transition in the TbFe11TiH single crystal. Hydrogenation lead to a change in sign of the magnetic anisotropy constant K3 and the magnetostriction constant λ 2 α,2.