Variation of structure and magnetic properties with thickness of thin Co59Fe26Ni15 filmsстатья

Статья опубликована в высокорейтинговом журнале

Информация о цитировании статьи получена из Scopus, Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 18 июля 2013 г.

Работа с статьей


[1] Variation of structure and magnetic properties with thickness of thin co59fe26ni15 films / N. G. Chechenin, E. H. van Voorthuysen, J. T. De Hosson, D. O. Boerma // Journal of Magnetism and Magnetic Materials. — 2005. — Vol. 290. — P. 1539–1542. Variations of phase composition and magnetic properties of electrodeposited nanocrystalline Co-Fe-Ni films with film thickness in the range of 50-500 nm were analyzed. The samples were magnetically soft with coercivity in the range H-c = 2-20 Oe and uni axial magnetic anisotropy up to H-k = 20 Oe. It was found that H-c decreases and H-k increases with increasing film thickness. The BCC phase dominates at small film thickness up to about 80 nm and the FCC phase increases when the film growths to a larger thickness. The increase of FCC phase correlates with the improvement of the ultrasoft magnetic properties. © 2004 Elsevier B.V. All rights reserved. [ DOI ]

Публикация в формате сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл сохранить в файл скрыть