MECHANICAL PROPERTIES OF CARBON STEEL DEPENDING ON THE RATE OF THE DOSE BUILD-UP OF NITROGEN AND ARGON IONSстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 20 марта 2018 г.
Аннотация:The effect of pulsed irradiation with argons and nitrogen ions on the mechanical properties, mor phology, and structure of the surface layers of carbon steel St3 (0.2% C, 0.4% Mn, 0.15% Si, and Fe for bal ance) has been investigated depending on the rate of dose buildup at an average ion current density of 10, 20, and 40 μA/cm2. It has been established that the fatigue life and microhardness of surface layers increase in the entire studied range of dose buildup rates. This seems to be due to the hardening of the surface layers, which resulted from the generation of radiation defects and the irradiationdynamic effect of fast ions. The sample irradiated by argon ions at the lowest of the selected dose buildup rates jav = 10 μA/cm2 withstands the largest number of cycles to failure.