Materials based on calcium pyrophosphate Са2Р2О7 with a molar ratio Ca/P=1 and calcium polyphosphate Са(РО3)2 (in an amount up to 50%), having a molar ratio Ca/P=0.5 meet the requirements that necessary for application in regenerative medicine. Calcium phosphates with a molar ratio Ca/P=1 (Са2Р2О7.хН2О, СаНРО4.2Н2О, СаНРО4) synthesized from solutions, in pastes, or in conditions of mechanical activation, can be precursors of calcium pyrophosphate Са2Р2О7. Calcium phosphates with a molar ratio Ca/P=0.5 (Са(РО3)2.хН2О, Са(Н2РО4).Н2О, Са(NH4)2P2O7, СаH2P2O7) can be precursors of calcium polyphosphate Са(РО3)2. Powder mixture comprising non direct precursors of the calcium pyrophosphate and polyphosphate phases at a given molar ratio in the range 0.5<Ca/P<1 can be used for production of ceramic materials in the system Са2Р2О7-Са(РО3)2. In such mixtures, the target phases are formed both as a result of thermal conversion and as a result of heterophase interaction. The work was supported by RFBR, projects # 18-29-11079, # 20-03-00550.
№ | Имя | Описание | Имя файла | Размер | Добавлен |
---|---|---|---|---|---|
1. | MST20_PrelimProgram.pdf | MST20_PrelimProgram.pdf | 1,5 МБ | 20 ноября 2020 [safronova] | |
2. | Safronova_HydroCaP_MST2020_www.pdf | Safronova_HydroCaP_MST2020_www.pdf | 135,2 КБ | 20 ноября 2020 [safronova] | |
3. | MST20_Next_Generation_Biomaterials_Poster_Session_www.pdf | MST20_Next_Generation_Biomaterials_Poster_Session_www.pdf | 132,7 КБ | 20 ноября 2020 [safronova] |