Crystallization conditions of LuAB in the pseudo-quaternary LuAl3(BO3)4 - K2Mo3O10 - B2O3 - Lu2O3 - Al2O3 flux system are reinvestigated. The Er(1.5at.%),Yb(12at.%):LuAl3(BO3)4 single crystal with dimension exceeding 10 mm which is suitable for optical measurements were grown using K2Mo3O10 - B2O3 - Lu2O3 - Al2O3 complex flux.