Thermoelectric properties of Au-based metallic glass at low temperaturesстатья
Информация о цитировании статьи получена из
Web of Science
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 19 сентября 2015 г.
Аннотация:Thermoelectric properties of Au49Cu26.9Ag5.5Pd2.3Si16.3 glassy alloy have been studied using electrical resistivity, thermal conductivity and Seebeck coefficient measurements over temperature range 2–390 K. At heating, resistivity ρ decreases in a power-law manner from residual value ρ0 ∼ 150 µΩ · cm. The temperature coefficient of resistivity, α = ρ−1(∂ρ/∂T ), is rather small and varies non-monotonously. Thermal conductivity κ rises linearly at low temperatures; it exhibits a plateau-like feature and sharply increases at elevated temperatures. Seebeck coefficient S increases with temperature and exhibits a characteristic “knee” feature. At elevated temperatures, S increases linearly with temperature but with a different slope. It total, thermoelectric properties of Au-based glassy alloy demonstrate behaviour of a highly disordered system in a most pronounced manner.